Crack initiation, small crack growth, and stress intensity factor in the very high cycle fatigue (VHCF) of wire arc additive manufactured (WAAM) nickel aluminum bronze (NAB) Article (Web of Science)

International Collaboration

cited authors

  • Mahtabi, Mohammadbagher; Roshan, Mojtaba; Shakil, Shawkat I.; Tridello, Andrea; Paolino, Davide S.; Bednarczyk, Wiktor; Haghshenas, Meysam

publication date

  • January 23, 2025

webpage

published in

category

keywords

  • NAB
  • Nickel aluminum bronze
  • Stress intensity factor
  • Very high cycle fatigue
  • Wire arc additive manufacturing

volume

  • 313